HYDROPOX EPG LV

Very low viscous flexible EP resin

  • Very low viscous for imbuing, filling and priming
  • Use also possible on moist substrates
  • Elastic behaviour when hardened
Mixture of A-and B-component
Processing temperature10 – 30°C (substrate temperature)
Mixing ratio A : B 3.9 : 1 (parts by vol.) 4 : 1 (p. b. weight)
Viscosity of mixture (23°C)~ 35 mPas (DIN EN ISO 2555)
Reaction data at 23°C
Pot-life~ 40 min (DIN EN 14022)
Dust-dry~ 6 h
Walkable~ 24 h
Final curing~ 7 d
Properties after curing
E-modulus~ 1,03 MPa (DIN EN ISO 527)
Tensile strength~ 0,30 N/mm2 (DIN EN ISO 527)
Elongation at break~ 45% (DIN EN ISO 527)