HYDROPOX EP 1 HV
High viscous 2 compoent injection resin based on Epoxy
- For friction-fit filling of cracks in reinforced concrete structures
- Use also possible on moist substrates
- For slender buildings
- High viscosity adjustment avoid uncontrolled flow
| Mixture of A-and B-component | |
|---|---|
| Processing temperature | 10 – 30°C (substrate temperature) |
| Viscosity of mixture (23°C) | ~ 400 mPas (DIN EN ISO 2555) |
| Mixing ratio A : B | 1.92 : 1 (parts by vol.) 2.27 : 1 (p. b. weight) |
| Reaction data at 23°C | |
| Pot-life | ~ 30 min (DIN EN 14022) |
| Final curing | ~ 7 d |
| Properties after curing | |
| Compressive strength | ~ 95 N/mm2 (DIN EN 12390) |
| E-modulus | ~ 190 MPa (DIN EN ISO 527) |
| Tensile strength | ~ 34 N/mm2 (DIN EN ISO 527) |
| Elongation at break | ~ 6% (DIN EN ISO 527) |