Rubber like elastic, multi-purpose 3-component acrylate gel

  • Very low viscous acrylate gel with high flexibility
  • Very good penetration, even in water filled cracks
  • Especially useful for massive elements
  • Long term stable. Proven stability of at least 19 years.
  • Groundwater friendly approved
  • German general building authority test certificate in combination with POLINIT

Mixture of A-and B-component:
Processing temperature5 – 40 °C (substrate temperature)
Viscosity of mixture (20°C)~ 2.5 mPas (DIN EN ISO 2555)
Reaction data at 20°C:
Pot-life~ 5 min (DIN EN 14022)
Final curing~ 10 min
Properties after curing:
Consistency rubber-like
E-modulus~ 0,13 MPa
Tensile strength~ 0,08 MPa
Elongation at break~ 290 %
Water absorption~ 20 %