PROOFMATE® FD membrane
System component of the PROOFMATE® FD system. Sealing membrane based on EPDM (ethylene propylene diene monomer).
- High elasticity even at low temperatures
- High mechanical properties due to vulcanisation
System component of the PROOFMATE® FD system. Sealing membrane based on EPDM (ethylene propylene diene monomer).
The patented Proofmate FD System is ideal for reliably sealing joints and can be used simply and effectively above and even under water.
Technical Data | |
---|---|
Material basis | EPDM |
Thickness | 1 mm |
Shore A hardness | 65 ± 5 (DIN ISO 7619-1) |
Temperature resistance | 150°C (long-term) 220°C (short-term) |
Tensile strength | 8,7 / 8,6 MPa (DIN EN 12311-2) |
Elongation at break | 531% / 483 % (DIN EN 12311-2) |
Joint peel strength | 69 N/50 mm (DIN EN 12316-2) |
Joint shear resistance | 282 N/50 mm (DIN EN 12317-2) |
Resistance to impact | 300 mm (DIN EN 12691) |
System component of the PROOFMATE® FD system. Single-com-ponent mastic adhesive and sealing compound based on SPO
(SPO = silane terminated polypropylenoxide)
Technical Data | |
---|---|
Material basis | SMP |
Consistency | pasty |
Spec. density (23°C) | ~ 1,5 g/cm3 (DIN EN ISO 2811-1) |
Dyn. viscosity (23°C) | ~ 2000 Pas (DIN EN ISO 2555) |
Reaction data at 23°C | |
Processing temperature | 5 – 40°C (substrate temperature) |
pH value | ~15 min (ASTM C679) |
Max. grain size | ~ 3 mm/24 h |
Cured adhesive | |
Tensile strength | ~ 1,3 N/mm2 (DIN EN ISO 527) |
Elongation at break | ~ 350 % (DIN EN ISO 527) |
Shore A hardness | ~ 40 (DIN ISO 7619-1) |
Temp. resistance | -30 bis +80°C |
Adhesion to concrete | > 1,65 N/mm2 (DIN EN 1542) |
SPACHTEL B3
metal spatular
Push-on roll
150 mm
Z2
hand press
PZ2
pneumatic hand press
For cleaning substrates and for bonding dusts and other contamination.
For priming heavily absorbent surfaces such as weathered concrete, brickwork, aerated concrete, eternit, natural stone, etc.