4 C injection gel on an acrylate or methacrylate basis which hardens to form a product with high compressive strength.

  • Low viscosity
  • Very good penetration
  • High final strength
  • Specific for stabilization of masonry or granular soil structures
Mixture of A-and B-component
Processing temperature5 – 40°C (substrate temperature)
Viscosity of mixture (20°C)~ 12 – 13 mPas (DIN EN ISO 2555)
Reaction data at 20°C
Pot-life~ 2 – 14 min (DIN EN 14022)
Final curing~ 10 -30 min
Properties after curing
Compressive strength (dried samples) (DIN EN 12190)
pure product~ 15,0 N/mm2
ith silica sand 0,1-0,3 mm~ 17,6 N/mm2
with silica sand 0,7-1,2 mm~ 20,0 N/mm2
Compressive strength (sample stored in water) (DIN EN 12190)
with silica sand 0,1-0,3 mm~ 5,0 N/mm2