SOLIDCRYL
4 C injection gel on an acrylate or methacrylate basis which hardens to form a product with high compressive strength.
- Low viscosity
- Very good penetration
- High final strength
- Specific for stabilization of masonry or granular soil structures
Mixture of A-and B-component | |
---|---|
Processing temperature | 5 – 40°C (substrate temperature) |
Viscosity of mixture (20°C) | ~ 12 – 13 mPas (DIN EN ISO 2555) |
Reaction data at 20°C | |
Pot-life | ~ 2 – 14 min (DIN EN 14022) |
Final curing | ~ 10 -30 min |
Properties after curing | |
Consistency | rubber-like |
Colour | opaque |
Compressive strength (dried samples) (DIN EN 12190) | |
pure product | ~ 15,0 N/mm2 |
ith silica sand 0,1-0,3 mm | ~ 17,6 N/mm2 |
with silica sand 0,7-1,2 mm | ~ 20,0 N/mm2 |
Compressive strength (sample stored in water) (DIN EN 12190) | |
with silica sand 0,1-0,3 mm | ~ 5,0 N/mm2 |